Technical data sheet PLUS 720 Polyester resin PROPERTIES PLUS 720 POLYESTER RESIN is a product for manual lamination. It contains a structural polyester resin with addition of appropriate catalysts. Use 50% of the benzoyl peroxide paste (NOVOL part no. 522) as the hardener. The product is intended for repairing large defects and rusted locations of car body parts made of metal sheets and laminates, as well as of boats, yachts and camping trailers. The resulting coating has a very good adhesion to the substrate. SUBSTRATES
dry sand with P80-P120 and degrease again with the PLUS 780
degrease, dry sand with P80 – P120, degrease again.
dry sand with P80 – P120 and clean of dust
degrease, mat with an abrasive needle cloth and degrease again
degrease, dry sand with P180 – P240, degrease again.
degrease, dry sand with P80 – P120, degrease again.
Do not apply the resin directly on top wash primers or one-component acrylic and nitrocellulose products.
MIXING RATIO APPLICATION LIFE FROM MIXING WITH THE HARDENER COATABILITY Technical Data Sheet LT-04-06 10/06/2013
Polyester putties, spray polyester filler, most primers, paints and varnishes
APPLICATION CONDITIONS
The minimum application temperature is +10°C
APPLICATION
Prepare the required piece of the mat. Trim the glass fiber mat so that it
extends approx. 2 cm beyond the limits of damage location.
Prepare the amount of the resin that can be consumed in approx. 10
minutes. Observe the required amount of hardener. Mix the components
thoroughly until a uniform colour is obtained. Weight quantity of
components: add 100 g of the resin to 2 – 3 g of Hardener.
The processing time is 10 to 15 minutes at 20°C.
Apply the resin with a brush on the clean area.
Apply the trimmed piece of mat, press down to the repaired area and saturate
Depending on the damage, several mat layers can be applied by repeating the
Sand the laminate surface with P80-P120 abrasive papers or fill out with the
Technical Data Sheet LT-04-06 10/06/2013 CAUTION:
The viscosity of the cured surface improves the adhesion of successive layers; if needed, viscosity can be cancelled by washing with the NC solvent. Do not put the leftover resin mixed with the hardener back into the can. The typical ratios used for lamination are: approx. 2 kg of the polyester resin per 1 kg of the carrier material (glass fiber mat or fabrics).
RELATED PRODUCTS
NOVOL part no. 5022 (50% benzoyl peroxide paste)
EQUIPMENT CLEANING STORAGE CONDITIONS
Store in a cool dry room, away from sources of fire and heat.
SHELF LIFE OTHER INFORMATION
The effectiveness of our systems results from laboratory research and many years of experience. The data contained herein meets the current knowledge about our products and their application potential. We ensure high quality, provided the user follows the instructions and the work is performed in accordance with good workmanship. It is necessary to do a test application of the product due to its potentially different reaction with different materials. We may not be held liable for defects if the final result was affected by factors beyond our control.
http://nyhealth.gov/diseases/communicable/chickenpox/fact_sheet.htmFurther information on chickenpox from Wadsworth Center for Laboratories and ResearchVersión en españolVaricela - Medline Plus Información de Salud para Usted What is chickenpox? Chickenpox is a highly contagious illness caused by the varicella-zoster virus (VZV), a type of herpes virus. It is often amild illness, character
I case report _ calcified mandibular molar Author_ Dr Rafaël Michiels, Belgium _Treatment and discussion A diagnostic radiograph (Fig. 1), which is essentialin determining the treatment strategy, was taken to visualise the extent of the lesion and the anatomy ofthe roots. The patient was then anesthetised by a loweralveolar nerve block with 4% articaine, 0.01mg/ml epinephrine (Sep